In the tech equivalent of a turkey dissing Thanksgiving dinners, Corning SVP Tony Tripeny has criticized sapphire as a material for protecting phone screens, coming up with a whole list of claimed drawbacks, reports CNET.

We see a lot of disadvantages of Sapphire versus Gorilla Glass. It’s about 10 times more expensive. It’s about 1.6 times heavier. It’s environmentally unfriendly. It takes about 100 times more energy to generate a Sapphire crystal than it does glass. It transmits less light which…means either dimmer devices or shorter battery life. It continues to break. I think while it’s a scratch resistant product it still breaks and our testing says that Gorilla Glass [can take] about 2.5 times more pressure that it can take.

Sapphire is far more resistant to scratches than Gorilla Glass, but Corning argue that it is more likely to be smashed.

Apple is expected to switch to a sapphire coating for the iPhone 6, manufacturing the material at the plant it jointly operates with GTAT in Arizona. While the material is indeed currently much more expensive than glass, it has been suggested that the costs could be substantially reduced with new production techniques.

Leave a Reply

Please log in using one of these methods to post your comment:

WordPress.com Logo

You are commenting using your WordPress.com account. Log Out / Change )

Twitter picture

You are commenting using your Twitter account. Log Out / Change )

Facebook photo

You are commenting using your Facebook account. Log Out / Change )

Google+ photo

You are commenting using your Google+ account. Log Out / Change )

Connecting to %s

16 Responses to “Gorilla Glass maker Corning (predictably) slams sapphire, saying weaker and dimmer”

  1. alphabetize1 says:

    I would just like a shatter resistant phone, I don’t really care what the material is.

  2. Fil Aperture says:

    It would of course be surprising if Tony Tripeny (is he with the mob?) said something like this: Sh*t man, that sapphire stuff Apple is prepping kicks our Gorilla Glass ass! It’s way better and I think we can wrap it up here. In German they say: gefundenes fressen…

  3. This isn’t just about sapphire versus Gorilla Glass. If you read up on GT Advanced Technologies and their current undertakings, you will see that there is a strong likelihood that solar charging technology will be part of that sapphire implementation.

    GT seems to have developed a process of using multiple layers of charging films, greatly enhancing charging efficiency. If this is what Apple is up to, the competition will look distinctly prehistoric – particularly since Apple has exclusive access to this new tech.

    http://seekingalpha.com/article/2062083-gt-advanced-technologies-is-ready-to-electrify-the-mobile-world

    • frankman91 says:

      No phone screen will EVER be solar. The surface area is not even close to what is needed to charge a phone; not even close.

      Most solar panels are about 9 watts per square foot, or 0.0625 watts per square inch. The iPhone 5 is 4.87×2.31 inches, or 11.249 square inches. That would give you 0.703 watts per hour in direct sunlight. At that rate the 5.45 watt/hr battery would take 7.75 hours to charge if it were switched off, drawing no standby power at all, sitting in direct sunlight. That is also making a very incorrect assumption that batteries charge at 100% efficiency, which they defiantly do not. Realistically, a switched off dead phone would take close to or more than 10-12 hours to charge in the best of conditions.

      The brief window that the phone is in not in your pocket would do absolutely nothing. Even if that “40% efficiency gain” by that multi-layer cell is true, it’s still falling very short from what you would need and would be absolutely no benefit to adding a solar panel to a cell phone that was the size of the screen.

  4. Sounds like a thin layer of sapphire on top of Gorilla Glass is the best solution?

    • Robert Nixon says:

      That would just make the screen dimmer, and the sapphire would still be prone to cracking, in which case you’d have to replace not just the sapphire, but the glass as well, since they would certainly be laminated together.

  5. scumbolt2014 says:

    Sapphire isn’t going to be used for iPhione screens. I think this is Corning helping Apple throw everyone off track.

  6. How many times do I have to explain on this site, the sapphire is NOT for iPhones.

    • Then what is it for?

      • bballpants says:

        iWatch. smaller surface, unscratcheable is more important than more light. Heavier doesn’t matter, in fact, it’s probably preferred as I like watches with a bit of heft. Economies of scale and research can develop further until sapphire BECOMES a suitable replacement for corning glass.

  7. I certainly think that Apple will not be putting your generic sapphire crystal onto the screen, they’ll be introducing something much better. “New production techniques” anyone?

  8. herb02135go says:

    9 to 5 Mac PREDICTABLY Promotes Untried Technology Alleged to be Used by Apple!

  9. bballpants says:

    “It’s about 10x more expensive.”
    So far. It’s not like Gorilla Glass was super cheap to make either. Apple. Economies of scale. Next.
    “It’s about 1.6x heavier”
    So? Still light.
    “Transmits less light. Breaks under less pressure”

    You know, all this means is that Sapphire isn’t ready for iPhone screens. It sounds ready for iWatch screens though. Less surface area means less weakpoints. Unscratchable for your watch is more important than allowing more light cuz you aren’t watching a movie on it!

    Plus it allows the technology to develop as iWatch iterates on its process.
    it’s a very apple thing to do.